水性烤漆用丙烯酸聚合物THYOSIL IM76
Thermosetting acrylic polymer 热固性丙烯酸聚合物
Description描述
THYOSIL IM76 is a DMEA (Dimethyilaminoethanol) neutralized resin solution.
THYOSIL IM76是DMEA(二甲基乙醇胺)中和的树脂溶液。
THYOSIL IM76 was specially developed for producing high resistance waterborne industrial enamels when it is formulated with monomeric melamine resins.
THYOSIL IM76 专为与氨基树脂配方用于生产高抗水性工业搪瓷和瓷漆而开发的。
THYOSIL IM76 plus Melanine resin leads to industrial baking enamels that feature outstanding spray characteristics and film properties.
THYOSIL IM76加氨基树脂 做出的工业烤漆具有优异的喷涂特性和成膜性。
Application 应用
Enamels based on THYOSIL IM76 solutions may be easily sprayed. They atomize finely and without sagging.
The enamels formulated on base of THYOSIL IM76, show similar properties to those obtained with solvent-borne systems and match or surpass those of other water reducible coatings made with high levels of co-solvents.
Additionally, enamels made with THYOSIL IM76 solutions, exhibit less sensitivity to variations in the environment conditions (temperature/relative humidity).
由IM76 做出的瓷漆有优异的喷涂性,雾化精细,不会流挂。与溶剂型产品相比显示出相似或优于它们的特性,同时所用助溶剂含量低。此外用IM76配置的瓷漆,对环境要求不苛刻(温度/相对湿度)。
Advantages 优势
ü Excellent gloss and film clarity.优异的光泽和成膜的清晰度
ü Outstanding sprayability. 出色的喷涂性
ü High solid enamels. 高固含瓷漆
ü Good enamel stability. 优良的瓷漆稳定性
ü Formulation simplicity. 配方简单
Typical properties典型值
These properties are typical, do not constitute specifications
Appearance外观 |
Clear yellowish liquid淡黄色液体 |
Solids % 固含量 |
30 |
Viscosity at 25°C (cP)粘度 |
Max. 500 |
pH |
7.2 |
Tg (°C) 固含量 |
76 |
Gloss White Enamel Starting Formulation光亮白色珐琅基础配方
WHITE GRINDING白色浆(白料) |
|||
Raw material 原料 |
(%) |
||
Water 水 |
18.10 |
||
THYOSIL IM76 (1) |
16.00 |
||
Butyl Glycol 丁基乙二醇(乙二醇丁醚) |
3.00 |
||
n-Butanol 正丁醇 |
2.50 |
||
DMAE 二甲基乙醇胺 |
0.40 |
||
TiO2 R-902 (2) 钛白粉 |
60.00 |
||
Total 总量 |
100.00 |
Manufacturing instructions 生产说明
a) Load water and THYOSIL IM76 into Cowles and stir at low speed.
将水和IM76加入釜中并低速搅拌
b) Load Butyl Glycol, n-Butanol and DMAE agent and mix for 5 minutes.
加入丁基乙二醇,正丁醇,二甲基乙醇胺,并混合5分钟
c) Increase Cowles speed, add slowly TiO2.提高搅拌速度并慢慢添加钛白粉
d) Disperse well until to homogeneity. 充分混合均匀
e) Increase Cowles speed to assure a good dispersion, checking with grinding gauge.
增加考尔斯的转速速度,确保了良好的分散性,磨削仪检查。
The dispersion needs to be homogeneous and glossy.
该分散体需要是均匀的,有光泽。
GLOSS WHITE ENAMEL白色亮漆 |
|||
Raw material原料 |
(%) |
||
THYOSIL IM76 (1) |
60.00 |
||
White Grinding 白色浆 |
30.00 |
||
Water 水 |
2.50 |
||
n-Butanol 正丁醇 |
0.70 |
||
Cymel 303 (2) 氨基树脂 |
6.00 |
||
PTSA (10%) ** 对甲苯磺酸 溶液(见注解) |
0.60 |
||
BYK-022 (3) 水性有机硅消泡剂 |
0.20 |
||
Total |
100.00 |
Manufacturing instructions生产说明
a) Load THYOSIL IM76 into Cowles and stir at low speed.将IM76加入釜内并低速搅拌
b) Add White Grinding and keep under stirring for 10 minutes. 加入白色浆并保持搅拌10分钟
c) Separately mix well, Water and n-Butanol increase a little the stirring speed.
提前预混水和正丁醇
d) Load slowly the mixture (C) onto the preparation (A).慢慢的将预混的水和正丁醇加入到釜内同时提高转速 。
e) Slowly add Cymel 303, PTSA (10%) and BYK-022.
慢慢加入氨基树脂,对甲苯磺酸溶液,以及消泡剂BYK-022 .
f) Keep under stirring for 15 minutes. 保持搅拌 15分钟
Typical Properties 典型值 |
Result |
Solid Content 固含量 |
45% |
Viscosity Ford Cup N°4 at 25°C 粘度 4号福特杯 |
120 sec秒 |
pH |
7.6 |
Application Test 应用测试
1. Moisture content of wood should be less than 2%. The wood was dried in a oven at 212°F.
木材水分应当低于 2% ,木材应当在100’C的烘箱中干燥。
2. once the MDF is fully dried, apply 1 layer by spray. 板材干燥后喷涂一遍
3. It is dried in oven for 5 minutes at 122 ° F. 在50’C的烘箱中干燥5分钟
4. Finally, it is cured for 30 minutes at 300 ° F.最后再在150’C的烘箱里固化30分钟
5. A minimum of two layers is suggested. 建议至少涂2遍。
Test 测试 |
Result结果 |
Resistance to household chemicals耐日用化学品 |
Very Good非常好 |
Gloss ( Glossmeter 60°) ASTM D523 光泽度 |
85 |
Hardness (ASTM D3363) 硬度 |
H |
Adhesion (ASTM D3359) 附着力 |
Excellent非常好 |
Coverage and leveling 覆盖率和流平性 |
Excellent非常好 |